Injection Pressure
Injection Cylinder Temperature
Mold Temperature
5000-10000
psi
160-200°F
50-60°F
34-69
MPa
71-93 °C
10-16 °C
PROPERTIES
& AVERAGE VALUES OF INJECTION
MOLDED SPECIMENS
PERMANENCE
ASTM
TEST
Chemical
Analysis
Elements
Fe
Cr
Mo
Ni
S
Mn
C
Range,
%
Balance
16-18
2-3
10-14
0.03
max
2.0
max
2.0
max
Feedstock
Specific Gravity
Moisture Content
Capillary Viscosity @ 1000
sec-1
4.8
6.8 – 7.2 %
1500 Poise
4.8
6.8 – 7.2 %
150 Pa-sec
D-792
NA
D-3835
SINTERED
PROPERTIES
(Sintered Properties are
dependant on sintering conditions)
Sintered Density
Sintered Shrinkage 0.40
in (10 mm) section
>92.8%
0.165 in/in
>92.8%
16.5%
D-955
MECHANICAL
(As
Sintered)
Ultimate Tensile Strength
Yield Strength (0.2% offset)
Tensile Elongation
Reduction in Area
79 ksi
34 ksi
88 %
59%
542 MPa
237 MPa
88 %
59 %
A-370
A-370
A-370
A-370
(Reference wrought)
Ultimate Tensile Strength
Yield Strength (0.2% offset)
Tensile Elongation
Reduction in Area
65 ksi
25 ksi
40 %
50%
450 MPa
170 MPa
40 %
50 %
A-370
A-370
A-370
A-370
Although all statements, information,
and data given herein are believed to be accurate,
they are presented without guarantee, warranty,
or responsibility of any kind, express or implied.
Statements or suggestions concerning possible
use of our products are made without representation
or warranty that any such use is free of patent
infringement, and are not suggestions to infringe
any patent. The user should not assume that
all safety measures are indicated, or that other
measures may not be required. Further information
concerning safe handling procedures can be obtained
from the Material Safety Data Sheet.
For further information please
contact Latitude Manufacturing Technologies.