Injection Pressure
Injection Cylinder Temperature
Mold Temperature
5000-10000
psi
160-200°F
50-60°F
34-69
MPa
71-93 °C
10-16 °C
PROPERTIES
& AVERAGE VALUES OF INJECTION
MOLDED SPECIMENS
PERMANENCE
ASTM
TEST
Chemical
Analysis
Elements
Fe
Cr
Ni
Cu
Nb
Si
Mn
C
O
Range,
%
Balance
15-16
4.0-4.5
3.0-3.5
0.15-0.45
0.7-0.9
0.7-0.9
0.4-0.06
<0.07
Feedstock
Specific Gravity
Moisture Content
Capillary Viscosity @ 1000
sec-1
4.6
7.8 – 8.2 %
1500 Poise
4.6
7.8 – 8.2 %
150 Pa-sec
D-792
NA
D-3835
SINTERED
PROPERTIES
(Sintered Properties are
dependant on sintering conditions)
Sintered Density
Sintered Shrinkage 0.40
in (10 mm) section
>98.5%
0.18 in/in
>98.5%
18%
D-955
MECHANICAL
(Sintered
and heat tempered @ 1025°C)
Ultimate Tensile Strength
Yield Strength (0.2% offset)
Tensile Elongation
Reduction in Area
Hardness, Rockwell C
152 ksi
142 ksi
10 %
23%
36
1048 MPa
979 MPa
10 %
23 %
36
A-370
A-370
A-370
A-370
E-18
(Sintered, HIP and heat tempered
@ 1025°C)
Ultimate Tensile Strength
Yield Strength (0.2% offset)
Tensile Elongation
Reduction in Area
Hardness, Rockwell C
Although all statements, information,
and data given herein are believed to be accurate,
they are presented without guarantee, warranty,
or responsibility of any kind, express or implied.
Statements or suggestions concerning possible
use of our products are made without representation
or warranty that any such use is free of patent
infringement, and are not suggestions to infringe
any patent. The user should not assume that
all safety measures are indicated, or that other
measures may not be required. Further information
concerning safe handling procedures can be obtained
from the Material Safety Data Sheet.
For further information please
contact Latitude Manufacturing Technologies.